HENDRI WIJAYA, NIM. 122014031 (2018) Pembuatan Bahan Bakar Cair Dari Pirolisis Plastik Jenis Polipropilena. Skripsi thesis, Universitas Muhammadiyah Palembang.

Preview	Text 122014031_BAB I_DAFTAR PUSTAKA.pdf Download (2MB) | Preview
	Text 122014031_BAB II_SAMPAI_BAB TERAKHIR.pdf Restricted to Repository staff only Download (5MB)

Abstract

ABSTRAK PEMBUATAN BAHAN BAKAR CAIR DARI PIROLISIS PLASTIK JENIS POLIPROPILENA ________________________________________ Hendri Wijaya Program Studi Teknik Kimia, Fakultas Teknik, Universitas Muhammadiyah Palembang, Indoenesia. e-mail hendri.wijaya18@gmail.com Sampah merupakan salah satu masalah serius di Indonesia yang belum terselesaikan secara optimal hingga saat ini, dimana komposisi terbanyak penimbunan sampah didominasi oleh sampah plastik. Tingginya penggunaan plastik dan lamanya waktu penguraian plastik dapat menimbulkan permasalahan yang besar sehingga diperlukan suatu cara untuk mengatasi masalah tersebut. Salah satunya adalah dengan cara mengkonversi sampah plastik menjadi bahan bakar cair dengan menggunakan proses pirolisis. Penelitian ini bertujuan untuk mengetahui pengaruh temperatur dan waktu pirolisis terhadap volume dan kualitas minyak yang dihasilkan. Penelitian ini menggunakan temperatur 250, 275, 300, 325 dan 350 oC yang dilakukan pada bulan Juni – Agustus 2018 di Laboratorium Kimia Analisa Universitas Muhammadiyah Palembang dan Laboratorium Pertamina RU III Plaju. Hasil penelitian menunjukkan bahwa temperatur dan waktu tidak memiliki pengaruh yang signifikan terhadap kualitas produk yang dihasilkan dari beberapa variasi temperatur yang diterapkan dalam penelitian ini, namun berpengaruh terhadap %Yield dari produk yang dihasilkan. %Yield maksimum berada di temperatur 350 oC sebesar 33,60%. Dari penelitian ini diharapkan untuk penelitian selanjutnya lebih memfokuskan pada produksi dan pengujian kualitas naptha dan diesel yang dihasilkan. Kata Kunci : Pirolisis, Polipropilena, Naptha, Kerosin, Diesel Kepustakaan : 24 (1983 – 2017) ABSTRACT PRODUCTION OF LIQUID FUELS FROM POLYPROPYLENE PLASTIC PYROLYZED________________________________________ Hendri Wijaya Department of Chemical Engineering, Faculty of Engineering, Muhammadiyah University, Palembang, Indonesia e-mail hendri.wijaya18@gmail.com Garbage is one of the serious problems in Indonesia which has not been optimally resolved to date, where the most composition of landfill is dominated by plastic waste. The high use of plastics and the length of time the plastic decomposition can cause major problems so that a method is needed to solve the problem. One of them is by converting plastic waste into liquid fuel using the pyrolysis process. This study aimed to determine the effect of pyrolysis temperature and time on the volume and quality of oil produced. This study used temperatures of 250, 275, 300, 325 and 350oC which were conducted in June - August 2018 at the Chemistry Laboratory for the Analysis of the Muhammadiyah University of Palembang and Laboratory of PT. Pertamina RU III Plaju. The results showed that temperature and time did not have a significant effect on product quality resulting from several temperature variations applied in this study, but had an effect on %Yield of the product produced. The maximum yield is at a temperature of 350oC by 33.60%. From this research, it is expected that further research will focus on producting and testing the quality of naphtha and diesel produced. Keywords : Pyrolysis, Polypropylene, Naphtha, Kerosene, Diesel Literature : 24 (1983 - 2017)

Item Type:	Thesis (Skripsi)
Additional Information:	1. Netty Herawati, ST., MT. 2. Atikah, ST., MT.
Uncontrolled Keywords:	Pyrolysis, Polypropylene, Naphtha, Kerosene, Diesel
Subjects:	Kimia > Teknologi Bahan Kimia Industri Kimia > Teknologi Kimia Kimia > Teknologi Minyak, Lemak, lilin dan Gas Industri
Divisions:	Fakultas Teknik > Teknik Kimia (S1)
Depositing User:	Mahasiswa Fakultas Teknik
Date Deposited:	03 Oct 2019 03:27
Last Modified:	03 Oct 2019 03:27
URI:	http://repository.um-palembang.ac.id/id/eprint/5562

Actions (login required)

View Item