IKA RIWANI, NIM. 112016109 (2020) PENGARUH PENAMBAHAN ABU SEKAM PADI DAN KAPUR TERHADAP KUAT TEKAN BETON DENGAN FC’25. Skripsi thesis, Universitas Muhammadiyah Palembang.
|
Text
112016109_BAB I_DAFTAR PUSTAKA.pdf Download (2MB) | Preview |
|
Text
112016109_ BAB II_SAMPAI BAB TERAKHIR.pdf Restricted to Repository staff only Download (2MB) |
Abstract
INTISARI Penelitian ini penulis mengambil Abu sekam padi dan kapur sebagai bahan tambah pada campuran beton . Dalam penelitian ini ,akan mengidentifikasi manfaat Abu Sekam Padi dan kapur sebagai material penambah semen pada beton . Abu sekam padi memiliki sifat sebagai pengikat jika dicampur dengan air,disamping itu juga merupakan pengikat pasir . Pasir silica mempunyai sifat hydropolic ,yaitu sifat yang dimiliki sebuah material untuk menarik dan mengikat air pada permukaan nya . Kapur merupakan salah satu komponen bahan bangunan yang berfungsi sebagai bahan perekat . kemapuan kapur ini dapat dimanfaat kan untuk menanbah campuran beton yang sebelumnya hanya menggunakan semen,pasir dan batu pecah . Tujuan penelitian ini adalah untuk mengetahui pengaruh penggunaan bahan addictive abu sekam padi dan kapur terhadap kuat tekan beton .persentase Kapur dan kapur bervariasi mulai darikapur 10% dan abu sekam padi 5%,7,5%,10% dan 12,5%. pengujian beton dilakukan pada umur beton 28 hari. Penelitian ini menggunakan benda uji berbentuk silinder dengan ukuran (15cmx30cm)dan sebanyak 30 benda uji dimana untuk setiap variasi sebanyak 5 benda uji . Dari penelitian dilaboratorium didapatkan nilai beton optimum terjadi pada variasi Kapur 10%+Abu Sekam Padi 5% dengan kuat tekan beton karakteristik 26,2 Mpa. Untuk nilai beton minimum dibeton normal + Kapur 10% dengan kuat tekan mecapai 22,2Mpa. Pada pemakaian Kapur 10%+abu sekam padi 7,5% adalah sebesar 24,92 Mpa,Kapur 10%+abu sekam padi 10% adalah sebesar 24,74 Mpa,dan kapur 10%+abu sekam padi 12,5% adalah sebesar 24,04 Mpa ABSTRACT This study the authors took rice husk ash and lime as an additive to the concrete mixture. In this study, we will identify the benefits of rice husk ash and lime as a material to add cement to concrete. Rice husk ash has properties as a binder when mixed with water, besides that it is also a binder of sand. Silica sand has hydropolic properties, which is the property of a material to attract and bind water to its surface. Lime is a component of building materials that functions as an adhesive. The ability of this lime can be used to add a concrete mixture that previously only used cement, sand and crushed stone. The purpose of this study was to determine the effect of using addictive materials for rice husk ash and lime on the compressive strength of concrete. The percentage of lime and lime varies from 10% lime and 5%, 7.5%, 10% and 12.5% rice husk ash. Concrete testing was carried out at 28 days of concrete. This study used a cylindrical specimen with a size (15cmx30cm) and as many as 30 specimens where for each variation there were 5 specimens. From the laboratory research, it was found that the optimum concrete value occurred at a variation of 10% Lime + 5% Rice Husk Ash with a characteristic concrete compressive strength of 26.2 Mpa. For the minimum value of concrete with normal concrete + 10% lime with a compressive strength of up to 22.2Mpa. In the use of 10% Lime + 7.5% rice husk ash is 24.92 Mpa, 10% Lime + 10% rice husk ash is 24.74 Mpa, and 10% lime + 12.5% rice husk ash is equal to 24.04 Mpa
Item Type: | Thesis (Skripsi) |
---|---|
Additional Information: | Pembimbing : 1. Mira Setiawati, S.T. M.T. 2. Ir. H. Zainul Bahri, M.T. |
Uncontrolled Keywords: | Abu sekam padi, Kapur,kuat tekan beton |
Subjects: | Teknik Sipil > Bahan-bahan Bangunan |
Divisions: | Fakultas Teknik > Teknik Sipil (S1) |
Depositing User: | Mahasiswa Fakultas Teknik |
Date Deposited: | 14 Oct 2020 00:44 |
Last Modified: | 14 Oct 2020 00:44 |
URI: | http://repository.um-palembang.ac.id/id/eprint/13236 |
Actions (login required)
View Item |